Environmental Ash Removal Method For Die Casting Aluminum
2022-08-30 18:12
Environmental Ash Removal Method For Die Casting Aluminum
For the ash removal of die-casting aluminum, I believe many manufacturers are worried because it is often difficult to operate, or it is not environmentally friendly, or even has great pollution, which is related to its specific composition. How should we operate to remove ash from die cast aluminum in an environmentally friendly manner?
Due to the high silicon content of die-casting aluminum alloy, the usual ash remover is not suitable. Moreover, many of the currently used ash removers for die-casting aluminum alloy contain hydrofluoric acid and other components, which have high requirements on operating equipment and protection, and complex wastewater treatment. Therefore, many manufacturers are developing more environmentally friendly die-casting aluminum ash remover, which can effectively remove the stains on the surface of die-casting aluminum workpieces and the black ash generated after chemical polishing and alkali corrosion, and produce a clean and bright surface, which has a strong ash removal and whitening effect on die-casting aluminum.
Let's take a look at the traditional die casting aluminum ash removal!
The alkali corrosion of die-casting aluminum will cause black ash. If you want to wash white, the traditional method is nitric acid + hydrofluoric acid at the ratio of 3:1. However, this process has high risk factor and large pollution, and is being phased out.
Benshan casting aluminum white ash remover does not contain hydrofluoric acid, and the reaction is mild in the process of casting aluminum ash removal, without harmful smoke volatilization, and the formula is environmental friendly. It has a good corrosion inhibition effect on aluminum alloys with high silicon content, and has little change on the size of precision castings. It is a very environmentally friendly ash removal process after alkali washing and chemical polishing of cast aluminum alloys.
Therefore, in the ash removal process of die-casting aluminum, many manufacturers gradually choose this kind of light acid ash removal method. After all, the traditional ash removal of die-casting aluminum is not only harmful to itself, but also not environmentally friendly, and the country and society are very excluded.
Related News
Read More >-
![What is the temperature for anodizing with dyes?]()
What is the temperature for anodizing with dyes?
1. Low-temperature anodizing (15℃ to 20℃): ● The oxide film is dense and has good wear resistance. 2. Medium-temperature anodizing (20℃ to 25℃): ● Wide range of applications and stable process. 3. High-temperature anodizing (25℃ to 30℃): ● Short production cycle and high efficiency.
-
![What dyes are used for anodizing aluminum?]()
What dyes are used for anodizing aluminum?
The dyes used for anodizing aluminum are: 1. Organic dyes (Organic dyes are dyes made through organic chemical reactions) ● Azo dyes: ● Anthraquinone dyes: ● Nitro dyes: 2. Inorganic dyes (Inorganic dyes are usually made of metal oxides or metal salts) ● Iron oxide: ● Chromates: ● Titanates:
-
![What are the key factors in the selection of aluminum anodizing dye?]()
What are the key factors in the selection of aluminum anodizing dye?
The color stability of anodizing dye is one of the first considerations in the selection. Products need to have long-lasting color brightness to ensure that they will not fade or change color during long-term use. Therefore, it is crucial to choose anodizing dye with high color stability.
-
![How is the corrosion resistance of products using anodizing dye?]()
How is the corrosion resistance of products using anodizing dye?
When scratches or damage occurs on the surface of the product treated with anodizing dye, the oxide film has a certain self-healing ability, which can repair the damaged parts through its own reoxidation and protect the aluminum-based material from further corrosion.
-
![How does the performance of anodizing dye change under different pH values?]()
How does the performance of anodizing dye change under different pH values?
● Acidic environment (PH<7): In an acidic environment, anodized dye may fade. ● Alkaline environment (PH>7): In an alkaline environment, some anodizing dye powders may change color or become ineffective.
-
![Can wax remover additive effectively remove stains from the surface of aluminum products?]()
Can wax remover additive effectively remove stains from the surface of aluminum products?
The main ingredients of wax remover additive usually include organic solvents and surfactants. These ingredients can chemically react or physically adsorb with surface stains to decompose or separate the stains, thereby achieving the purpose of removal.
-
![What is the effect of wax remover additive on the wear resistance of aluminum products?]()
What is the effect of wax remover additive on the wear resistance of aluminum products?
The chemical composition of wax remover additive may enhance the hardness and wear resistance of aluminum surface, making it more resistant to friction and wear; while other chemical compositions may reduce the wear resistance of aluminum products, making them more susceptible to surface damage.
-
![What are the methods and steps of using sealing additive agent?]()
What are the methods and steps of using sealing additive agent?
The aluminum product after the immersion treatment needs to be dried and cured so that the sealant forms a dense sealing film and improves the sealing and corrosion resistance of the oxide layer.